LCD&DLP 3D Resin
405nm
SLA 3D Resin
355nm
-
-
LCD&DLP 3D Resin
For 405nm LCD&DLP 3D Printer | Outstanding performance, excellent detail
- General Resin Series
- Engineering Resin Series
- Shoe Resin Series
- Dental Resin Series
- Clear Resin Series
-
GM1811
53.7MPa
Tensile Strength
3160MPa
Tensile Modulus
78.6MPa
Flexural Strength
2450MPa
Flexural Modulus
5.1%
Elongation at Break
31J/m
Izod Impact(Notched)
59.1℃
Heat Deflection Temperature
81
Hardness(Shore D)
Tough white resin
MS1920
54MPa
Tensile Strength
2200MPa
Tensile Modulus
93MPa
Flexural Strength
2465MPa
Flexural Modulus
13%
Elongation at Break
32J/m
Izod Impact(Notched)
59℃
Heat Deflection Temperature
87
Hardness(Shore D)
Good detail performance
GM1618
42MPa
Tensile Strength
2280MPa
Tensile Modulus
80MPa
Flexural Strength
1860MPa
Flexural Modulus
8%
Elongation at Break
32J/m
Izod Impact(Notched)
49℃
Heat Deflection Temperature
78
Hardness(Shore D)
Classical and good quality
-
GM1728
62.4MPa
Tensile Strength
3200MPa
Tensile Modulus
83.1MPa
Flexural Strength
2390MPa
Flexural Modulus
6.8%
Elongation at Break
42J/m
Izod Impact(Notched)
56.4℃
Heat Deflection Temperature
83
Hardness(Shore D)
High toughness and strength
SoftX1658
3-4MPa
Tensile Strength
40-50MPa
Tensile Modulus
2-3MPa
Flexural Strength
80-100MPa
Flexural Modulus
51%
Elongation at Break
120-150J/m
Izod Impact(Notched)
/
Heat Deflection Temperature
90
Hardness(Shore A)
PU-like soft resin
Thermo1638
64MPa
Tensile Strength
2846MPa
Tensile Modulus
112MPa
Flexural Strength
2600MPa
Flexural Modulus
4%
Elongation at Break
19J/m
Izod Impact(Notched)
70℃
Heat Deflection Temperature
88
Hardness(Shore D)
High temperature resistance
Crycast2101
49MPa
Tensile Strength
2730MPa
Tensile Modulus
80MPa
Flexural Strength
2360MPa
Flexural Modulus
15%
Elongation at Break
22J/m
Izod Impact(Notched)
53℃
Heat Deflection Temperature
84
Hardness(Shore D)
Casting with no resident ash
-
MS1920
54MPa
Tensile Strength
2200MPa
Tensile Modulus
93MPa
Flexural Strength
2465MPa
Flexural Modulus
13%
Elongation at Break
32J/m
Izod Impact(Notched)
59℃
Heat Deflection Temperature
87
Hardness(Shore D)
Outstanding detail performance
-
D2000
52MPa
Tensile Strength
2200MPa
Tensile Modulus
98MPa
Flexural Strength
2500MPa
Flexural Modulus
9%
Elongation at Break
32J/m
Izod Impact(Notched)
54℃
Heat Deflection Temperature
84
Hardness(Shore D)
Dental model
-
Crysplus1801
48MPa
Tensile Strength
2200MPa
Tensile Modulus
86MPa
Flexural Strength
2100MPa
Flexural Modulus
12%
Elongation at Break
28J/m
Izod Impact(Notched)
52℃
Heat Deflection Temperature
86
Hardness(Shore D)
High transparency
- General Resin Series
- Engineering Resin Series
- Jewelry&Sculpt Resin Series
- Dental Resin Series
- Clear Resin Series
-
X110
40.2MPa
Tensile Strength
2100-2300MPa
Tensile Modulus
72MPa
Flexural Strength
1800-1900MPa
Flexural Modulus
19%
Elongation at Break
35J/m
Izod Impact(Notched)
52℃
Heat Deflection Temperature
84
Hardness(Shore D)
Fine and smooth texture
Gray White
W900
44MPa
Tensile Strength
2200-2300MPa
Tensile Modulus
76MPa
Flexural Strength
2000-2100MPa
Flexural Modulus
16%
Elongation at Break
38J/m
Izod Impact(Notched)
54℃
Heat Deflection Temperature
86
Hardness(Shore D)
Wash with water directly
Orange Red
Jade white Light grey
25.6MPa
Tensile Strength
511MPa
Tensile Modulus
99.1MPa
Flexural Strength
2225MPa
Flexural Modulus
6.8%
Elongation at Break
23.1J/m
Izod Impact(Notched)
92℃
Heat Deflection Temperature
89
Hardness(Shore D)
Draft300
High speed printing
-
Rigid110
42.7MPa
Tensile Strength
2300-2500MPa
Tensile Modulus
77.4MPa
Flexural Strength
1922MPa
Flexural Modulus
20%
Elongation at Break
39.3J/m
Izod Impact(Notched)
/
Heat Deflection Temperature
85
Hardness(Shore D)
High Resolution and Rigidity
Gray White Black Blue Skin
Elastic600
5-6MPa
Tensile Strength
/
Tensile Modulus
90-110MPa
Flexural Strength
/
Flexural Modulus
45-55%
Elongation at Break
140-150J/m
Izod Impact(Notched)
56℃
Heat Deflection Temperature
30
Hardness(Shore D)
Soft and elastic
Black White
ABS110
65MPa
Tensile Strength
3000MPa
Tensile Modulus
84.2MPa
Flexural Strength
2420MPa
Flexural Modulus
84%
Elongation at Break
49J/m
Izod Impact(Notched)
60℃
Heat Deflection Temperature
84
Hardness(Shore D)
High izod impact
Black
-
RC900
42MPa
Tensile Strength
2200-2300MPa
Tensile Modulus
77MPa
Flexural Strength
2000MPa
Flexural Modulus
19%
Elongation at Break
38J/m
Izod Impact(Notched)
48℃
Heat Deflection Temperature
81
Hardness(Shore D)
Outstanding Detail Performance
Orange Red
RC800
42MPa
Tensile Strength
2200-2300MPa
Tensile Modulus
77MPa
Flexural Strength
2000MPa
Flexural Modulus
19%
Elongation at Break
38J/m
Izod Impact(Notched)
54℃
Heat Deflection Temperature
83
Hardness(Shore D)
For models with tiny detail
Orange Red
RC600
42MPa
Tensile Strength
2200-2300MPa
Tensile Modulus
76MPa
Flexural Strength
1890MPa
Flexural Modulus
19%
Elongation at Break
38J/m
Izod Impact(Notched)
49℃
Heat Deflection Temperature
82
Hardness(Shore D)
Good surface texture
Orange Red
-
DM550
45MPa
Tensile Strength
2500-2600MPa
Tensile Modulus
79MPa
Flexural Strength
2100MPa
Flexural Modulus
21%
Elongation at Break
37J/m
Izod Impact(Notched)
54℃
Heat Deflection Temperature
85
Hardness(Shore D)
Dental model
Skin
-
Crys100
43MPa
Tensile Strength
2200-2300MPa
Tensile Modulus
75MPa
Flexural Strength
2000MPa
Flexural Modulus
19%
Elongation at Break
35J/m
Izod Impact(Notched)
50℃
Heat Deflection Temperature
83
Hardness(Shore D)
Transparent and beautiful
Transparent